310S Stainless Steel Grad

 

Kompożizzjoni Kimika

Il-kompożizzjoni kimika tal-istainless steel tat-tip 310 hija elenkata fit-tabella li ġejja.

Tip 310 Stainless Steel Kompożizzjoni Kimika, %
Standard ASTM	AISI (UNS)	C, Inqas minn jew ugwali għal	Si, Inqas minn jew ugwali għal	Mn, Inqas minn jew ugwali għal	P, Inqas minn jew ugwali għal	S, Inqas minn jew ugwali għal	Cr	Ni	Elementi Oħra
ASTM A240/A240M; ASTM A276/A276M; ASTM A314; ASTM A167; ASTM A479/A479M ASTM A580/A580M; ASTM A473; ASTM A959 SAE J405;	310 (UNS S31000)	0.25	1.50	2.00	0.045	0.03	24.0-26.0	19.0-22.0	–
	310S (UNS S31008)	0.08	1.50	2.00	0.045	0.03	24.0-26.0	19.0-22.0	–
	310H (UNS S31009)	0.04-0.10	0.75 (1.00)	2.00	0.045	0.03	24.0-26.0	19.0-22.0	–
	310Cb (UNS S31040)	0.08	1.5	2.00	0.045	0.03	24.0-26.0	19.0-22.0	Nb, 10×C-1.10
	310HCb (UNS S31041)	0.04-0.10	0.75	2.00	0.045	0.03	24.0-26.0	19.0-22.0	Nb, 10×C-1.10

Proprjetajiet Fiżiċi

Il-proprjetajiet fiżiċi tal-istainless steel tat-tip 310 huma elenkati fit-tabella hawn taħt bħal densità, punt tat-tidwib, sħana speċifika, resistività elettrika, modulu elastiku (modulu ta 'elastiċità), konduttività termali u koeffiċjent ta' espansjoni termali (CTE).

Noti:

10^-6·K^-1 = 10^-6/K

1 Ω·mm²/m=1 μΩ·m

1 g/ċm3=1 kg/dm3=1000 kg/m3

1 GPa=1 kN/mm2

1 MPa=1 N/mm2

Tip 310 Proprjetajiet Fiżiċi
Densità, g/cm3 (lb/in3)	8.0 (0.29)
Punt tat-tidwib, grad (grad F)	1400-1450 (2550-2650)
Kapaċità speċifika tas-sħana, J/kg·K (Btu/lb · grad F)	500 (0.12) fi 20 grad (68 grad F)
Reżistività elettrika, μΩ·m	0.78 f'20 grad (68 grad F)
Permeabilità manjetika	1.02 (Approssimattiv)
Modulu elastiku (Modulu ta 'Elastiċità), Gpa (106psi)	200 (29.0)
Konduttività termali, W/m·K (Btu/ft · h · grad F)	14.2 (8.2) f'100 grad (212 grad F)
	18.7 (10.8) f'500 grad (932 grad F)
Koeffiċjent ta 'espansjoni termali (CTE), 10-6/K (μin./in. · grad F)	15.9 (8.8) f'0-100 grad (32-212 grad F)
	16.2 (9.0) f'0-315 grad (32-600 grad F)
	17.0 (9.4) f'0-538 grad (32-1000 grad F)