🧪 Kompożizzjoni Kimika
| Element | Kompożizzjoni (%) |
|---|---|
| Karbonju (C) | ≤ 0.15 |
| Manganiż (Mn) | ≤ 1.00 |
| Silikon (Si) | ≤ 1.00 |
| Fosfru (P) | ≤ 0.040 |
| Kubrit (S) | ≤ 0.030 |
| Kromju (Cr) | 11.5 - 13.5 |
| Nikil (Ni) | ≤ 0.75 |
| Ħadid (Fe) | Bilanċ |
⚙️ Proprjetajiet Mekkaniċi
| Proprjetà | Kundizzjoni Ittemprat | Mwebbsa & Ittemprat |
|---|---|---|
| Qawwa tat-tensjoni | 485-620 MPa | 725-850 MPa |
| Qawwa tar-Rendiment (0.2% offset) | 275-415 MPa | 550-690 MPa |
| Titwil (50mm) | ≥ 20% | ≥ 15% |
| Tnaqqis taż-Żona | ≥ 50% | ≥ 45% |
| Ebusija (Brinell) | 155-217 HB | 235-285 HB |
| Ebusija (Rockwell C) | - | 22-32 HRC |
| Enerġija tal-Impatt (Charpy V-talja) | 54-81 J | 27-54 J |
| Limitu ta' Għeja (10&sup7; ċikli) | 240 MPa | 360 MPa |
🔬 Proprjetajiet Fiżiċi
| Proprjetà | Valur |
|---|---|
| Densità | 7.75 g/ċm³ |
| Punt tat-tidwib | 1480-1530°C |
| Sħana speċifika (20°C) | 460 J/kg·K |
| Konduttività Termali (100°C) | 24.9 W/m·K |
| Espansjoni Termali (20-100°C) | 9.9×10-6/K |
| Espansjoni Termali (20-500°C) | 11.2×10-6/K |
| Reżistività Elettrika (20°C) | 0.57 µΩ·m |
| Permeabilità manjetika | Ferromanjetiku |
| Modulu ta 'Elastiċità | 200 GPa |
| Proporzjon ta' Poisson | 0.27-0.30 |
📏 Speċifikazzjonijiet tal-Prodott
| Formola tal-Prodott | Firxa Daqs | Standards |
|---|---|---|
| Vireg tondi | 6-300mm dijametru | ASTM A276, A479 |
| Pjazza Bars | 10-150mm | ASTM A276 |
| Ċatti Bars | 3-100mm ħxuna, sa 300mm wiesgħa | ASTM A276 |
| Folji | 0.5-6mm ħxuna, sa 2000mm wiesgħa | ASTM A240 |
| Pjanċi | 6-100mm ħxuna, sa 3000mm wiesgħa | ASTM A240 |
| Tubi | 6-219mm OD, ħajt 0.5-20mm | ASTM A268 |
| Finish tal-wiċċ | Irrumblat bis-sħana, miġbud fil-kesħa, illustrat | 2B, BA, Nru.4, Nru.8 |
| Tolleranza | ±0.1mm sa ±1.0mm | EN 10029, ASTM A480 |