L-istainless steel 304 huwa prova tas-sadid?
Feb 25, 2026
Ħalli messaġġ
Kompożizzjoni Kimika ta 'Stainless Steel 304
Tabella 1.Kompożizzjoni kimika għal 304 ligi tal-istainless steel
|
% |
304 |
304L |
304H |
|
C |
0.0 - 0.07 |
0.0 - 0.03 |
0.04 - 0.08 |
|
Mn |
0.0 - 2.0 |
0.0 - 2.00 |
0.0 - 2.0 |
|
Si |
0.0 - 1.00 |
0.0 - 1.00 |
0.0 - 1.0 |
|
P |
0.0 - 0.05 |
0.0 - 0.05 |
0.0 - 0.04 |
|
S |
0.0 - 0.03 |
0.0 - 0.02 |
0.0 - 0.02 |
|
Cr |
17.50 - 19.50 |
17.50 - 19.50 |
17.00 - 19.00 |
|
Ni |
8.00 - 10.50 |
8.00 - 10.50 |
8.00 - 11.00 |
|
Fe |
Bilanċ |
Bilanċ |
Bilanċ |
|
N |
0.0-0.11 |
0.0-0.11 |
0.0 - 0.10 |
Proprjetajiet ta 'Stainless Steel 304
Proprjetajiet mekkaniċi ta 'Stainless Steel 304
Tabella 2a.Proprjetajiet mekkaniċi għal folja ta' liegi ta' l-istainless steel 304 - sa 8 mm ħxuna
|
Grad |
304 |
304L |
304H |
|
Qawwa tat-tensjoni (MPa) |
540 - 750 |
520 - 700 |
- |
|
Stress tal-Prova (MPa) |
230 Min |
220 Min |
- |
|
Titwil A50 mm |
45 Min % |
45 Min % |
- |
Tabella 2b.Proprjetajiet mekkaniċi għal pjanċa ta' liegi tal-istainless steel 304 - minn 8 - 75 mm ħxuna
|
Grad |
304 |
304L |
304H |
|
Qawwa tat-tensjoni (MPa) |
520 - 720 |
500 - 700 |
- |
|
Stress tal-Prova (MPa) |
210 Min |
200 Min |
- |
|
Titwil A5 |
45 Min % |
45 Min % |
- |
Tabella 2c.Proprjetajiet mekkaniċi għal 304 ligi tal-istainless steel - bar u sezzjoni sa 160 mm dijametru/ħxuna
|
Grad |
304 |
304L |
304H |
|
Qawwa tat-tensjoni (MPa) |
500 - 700 |
500 - 700 |
500 - 700 |
|
Stress tal-Prova (MPa) |
190 |
175 Min |
185 Min |
|
Titwil A50 mm |
45 Min % |
45 Min % |
40 Min % |
|
Ebusija Brinell |
215 Max HB |
215 Max HB |
- |