X'inhu 201 Stainless Steel?
Mar 23, 2026
Ħalli messaġġ
Standards u Gradi Ekwivalenti
| ASTM | JIS | UNS | MT | DIN | GOST | GB |
|---|---|---|---|---|---|---|
201 | SUS201 | S20100 | 1.4372 | X12CrMnNiN17-7-5 | 12Х15Г9НД | 12Cr17Mn6Ni5N |
Kompożizzjoni Kimika ta '201 Stainless
| Grad | Standard | C | Cr | Ni | Mn | Si | P | S | Mo | Fe |
|---|---|---|---|---|---|---|---|---|---|---|
201 | ASTM A240 | ≤0.15 | 16.0–18.0 | 3.5–5.5 | 5.5–7.5 | ≤1.0 | ≤0.06 | ≤0.03 | – | Bilanċ |
1.4372 | EN 10088-2 | ≤0.15 | 16.0–18.0 | 3.5–5.5 | 5.5–7.5 | ≤1.0 | ≤0.06 | ≤0.03 | – | Bilanċ |
SUS201 | JIS G 4304 | ≤0.15 | 16.0–18.0 | 3.5–5.5 | 5.5–7.5 | ≤1.0 | ≤0.06 | ≤0.03 | – | Bilanċ |
Meta mqabbel ma '304, in-nikil jitnaqqas filwaqt li jiżdied il-manganiż, li jnaqqas l-ispiża iżda jillimita r-reżistenza għall-korrużjoni f'ambjenti aggressivi.
Proprjetajiet Mekkaniċi
| Grad | Standard | Qawwa tat-tensjoni | Qawwa tar-Rendiment | Titwil | Ebusija |
|---|---|---|---|---|---|
201 | ASTM A240 | ≥ 520 MPa | ≥ 275 MPa | ≥ 40% | ≤ 95 HBW |
1.4372 | EN 10088-2 | ≥ 520 MPa | ≥ 275 MPa | ≥ 40% | ≤ 95 HBW |
SUS201 | JIS G 4304 | ≥ 520 MPa | ≥ 275 MPa | ≥ 40% | ≤ 95 HBW |
Varjanti ta '201 Stainless Steel: J1, J2, J4
Biex tgħinek tagħżel aħjar, hawn kif J1, J2, u J4 huma differenti:
| Varjant | Aġġustamenti Tipiċi ta' Kompożizzjoni | Karatteristiċi | Użi Tipiċi |
|---|---|---|---|
201 J1 | Ni ~ 4.0–4.5%, Cu ~ 1.5% | Formabilità eċċellenti u kapaċità ta 'stirar | Utensili tal-kċina, sinkijiet, oġġetti tal-kċina |
201 J2 | C kemxejn ogħla, Cu aktar baxx | Saħħa ogħla, inqas elongazzjoni | titwil Qafliet, profili industrijali, kostruzzjoni |
201 J4 | Lower Ni (~3.5%), Mn ogħla, Cu ~1.5% | L-aħjar għal finituri dekorattivi, spiża aktar baxxa | Bibien, pannelli, dekorazzjoni ta 'ġewwa |
Ibgħat l-inkjesta